Oxide coatings for fluoride glass

ABSTRACT

Non-oxide or heavy metal fluoride glass optical fiber with or without a cladding and coated with an outer layer of an oxide glass having a glass transition temperature of less than 400° C. and a thermal expansion coefficient of less than about 19×10 -6  ° C. -1 . Also, a method of making and providing such coatings on non-oxide or fluoride glass, and fiber optic products prepared by such methods.

TECHNICAL FIELD

This invention relates to new coating compositions for providing various clear and opaque protective coatings for non-oxide (e.g., fluoride) glass optical fibers for improving the performance thereof.

BACKGROUND ART

Fluoride fiber has rapidly developed into a very useful medium for mid-IR transmission, with great potential for long distance IR communication. Fluoride fibers are predicted to have intrinsic losses less than those of silica fibers, which might increase significantly the repeator spacing in long fiberoptic links, especially in undersea cables. Unfortunately, the chemical durability of fluoride glasses is low and, therefore, the mechanical failure of fluoride fibers over extended periods of time will be more likely than with silica fibers. Liquid and gaseous water react readily with the fiber surface, leading to the formation of surface flaws and stress corrosion.

Two solutions to the corrosion/strength problem have been proposed. The first one is to protect the fiber surface by an impervious hermetic coating, so that the water or moisture would be prevented from reaching the fiber surface. Various types of plastic, metal and ceramic hermetic coatings have been described in the prior art.

The second solution is to make the core glass of mixed fluorides and cladding of chalcogenide glass.Chalcogenide glasses have been chemical durability than fluoride glasses (A. Nakata, J. Lau and J. D. Mackenzie, Materials Science Forum, 6, 717 (1985). The principal disadvantages of chalcogenide glass is its high level of toxicity, which is very disturbing in the case of medical or surgical applications.

Another problem, common to both fluoride and chalcogenide glasses, is the necessity to protect them during the fiber draw by an inert atmosphere to avoid surface reaction with moisture or oxygen. In fluoride glasses reaction with moisture can cause surface defects and initiate crystallization (G. S. Sapsford, N. J. Pitt and J. D. Morris, paper presented at Soc. of Glass Technology Meeting, Peebles, Scotland, June 12, 1986; H. Schneider, A. Schoberth and A. Staudt, paper presented at 4th Int. Symposium on Halide Glasses, Monterey, Calif., Jan. 28, 1987).

A common way of protecting fluoride fibers today is by applying a thin layer (5-30 microns) of a Teflon FEP coating. This layer enables the fiber to be handled but does not protect it for long periods of time against moisture, which can migrate through the porous coating.

The object of this invention is to protect the fluoride fiber by providing an additional overcladding of oxide glass or other hermetic coatings which are compatible with the fluoride glass.

SUMMARY OF THE INVENTION

The present invention relates to a coated non-oxide (e.g., fluoride) glass optical fiber comprised of a core of a non-oxide glass, such as a heavy metal fluoride, and a coating of a metal oxide glass which has a similar glass transition temperature (typically in the range 200°-400° C.) and thermal expansion coefficient (typically in the range of 15 to 19×10⁻⁶ ° C.⁻¹). Preferably, the coating is an alkali borophosphate or an alkali-Group II metal phosphate material, wherein the viscosity of the oxide coating material at the draw temperature is approximately the same as the viscosity of the non-oxide glass, and the oxide coating can have an index of refraction which is less than that of the non-oxide glass core. If desired, a cladding of a different glass can be added between the core and the oxide glass coating.

The invention also relates to a method for making a non-oxide glass optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises drawing the non-oxide glass fiber from a draw furnace, possible without a protective atmosphere, from a perform which is comprised of a non-oxide glass core and a protective overclad of oxide glass having a glass transition temperature below about 400° C., a thermal expansion coefficient in the range of 15 to 19×10⁻⁶ ° C.⁻¹ and a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain a coated optical fiber. Typically, the fiber is drawn in a range between 300° and 425° C.

The preform may be made by initially melting the oxide glass coating; casting the molten oxide glass into a rotating mold to form a tube of oxide glass, and placing a molten non-oxide glass composition into the tube of oxide glass to form the preform. Also, the preform can include a non-oxide glass cladding between the non-oxide glass core and oxide glass coating, which cladding is added to the preform after the metal oxide glass tube is formed. The metal oxide glass compositions described above are preferably used in this preform.

An additional embodiment of the invention relates to a method for imparting high strength properties as well as resistance to water or moisture to a non-oxide or heavy metal fluoride glass fiber while retaining the optical properties of the fiber, which method comprises coupling an outer layer of a protective metal oxide glass overclad of the compositions described above the optical fiber.

The coated non-oxide fluoride glass optical fibers produced by the previously described methods represent another embodiment of the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention relates to a new construction for non-oxide glass optical fiber, and particularly for fluoride glass optical fiber: a conventional heavy metal fluoride glass core and clad are coupled with an outer layer of protective oxide glass. Such oxide coated fluoride fibers possess the following advantages:

(1) they retain the optical properties of the conventional heavy metal fluoride glass fiber, while the oxide coating imparts the strength and mechanical properties of the oxide glass to the fiber;

(2) the oxide coating precludes surface hydrolysis and crystallization of the fluoride glass core during the drawing operation;

(3) the need for a dry protective atmosphere over the fluoride fiber during the drawing operation is reduced or eliminated;

(4) preforms with oxide coatings can be made larger than preforms containing only fluoride glass because of the oxide's greater stability against crystallization and higher thermal conductivity. This allows greater lengths of fiber to be produced from the preform while lowering the cost of the materials; and

(5) they retain the physical properties of oxide glass cladding, which makes conventional removal of polymer coatings easier compared to those on fluoride glass claddings.

The oxide glass for the coating is chosen from a variety of known glass compositions having similar viscosity and thermal expansion properties as the fluoride core and clad. This means that the glass transformation temperature (T_(g)) is below about 400° C. and preferably between about 200° and 300° C., preferably between 230° and 290° C. Also, the thermal expansion coefficient of the oxide glass should be similar to or lower than that of the fluoride glass, i.e., below about 19×10⁻⁶ ° C.⁻¹ and preferably between 15×10⁻⁶ ° C.⁻¹ and 19×10⁻⁶ ° C.⁻¹. Also, the log of viscosity of the oxide glass coating should range from about 10⁵ to 10⁶ poise at the fluoride fiber drawing temperature for optimum compatibility of the cladding with the fluoride glass core.

This oxide glass layer protects from reaction with water the fluoride glass during the entire process of preform handling, fiber drawing, and fiber usage. This reduces and may eliminate, therefore, the need for a protective atmosphere during the fiber draw and simplifies the draw furnace arrangement. Another advantage of this coated fluoride glass composite is in the increased durability and strength during the fiber lifetime. Incorporation of other oxides, such as A1₂ O₃, will increase the chemical durability of the oxide glass. Lowering the thermal expansion coefficient of the oxide clad relative to the fluoride core can increase the fiber strength by placing the cladding under compression.

Oxide glasses matching the above requirements can be chosen from the group of alkali borophosphates, for example, K₂ O-B₂ O₃ -P₂ O₅, Na₂ O-B₂ O₃ -P₂ O₅, Li₂ O-B₂ O₃ -P₂ O₅ (N. H. Ray et al., Glass Technology, 17, 66 (1976)) or from the group of alkali -Group II metal phosphate glasses (J.E. Shelby and J.A. Wilder, Journal of the American Ceramic Society, 67 438 (1984)--). In these glasses, the relative proportion of components preferably is as follows:

    ______________________________________                                         alkali oxides      20 to 50 mol %                                              Group II-A or II-B                                                             metal oxide or boron oxides                                                                       10 to 30 mol %                                              phosphorous pentoxide                                                                             30 to 60 mol %                                              ______________________________________                                    

The most preferred alkali oxides are sodium, potassium and lithium. Although a single alkali oxide can be used for simplicity of formulation, mixtures of two or more of such alkali oxides can be used if desired. The preferred Group II metal oxide components include ZnO and BaO. Alternatively, boron oxide can be used instead of or with the alkaline earth oxide with similar results. As noted above, other oxides can be added for imparting particular properties or performance characteristics to the material.

Generally, oxide compositions may include

    ______________________________________                                         Li.sub.2 O     0-22     mol %                                                  Na.sub.2 O     15-42    mol %                                                  K.sub.2 O      0-22     mol %                                                  ZnO            15-20    mol %                                                  P.sub.2 O.sub.5                                                                               40-55%   mol %                                                  Other (CaO, Al.sub.2 O.sub.3, ZrO.sub.2, GeO.sub.2, SiO.sub.2, TiO.sub.2,      etc.) 0-10 mol %                                                               ______________________________________                                    

Other (CaO, Al₂ O₃, Zro₂, Geo₂, SiO₂, TiO₂, etc.) 0-10 mol % provided that the sum of Li₂ O+Na₂ O+ZnO+P₂ O₅ is greater than 90 mol %.

The most advantageous formulations for the glass oxide claddings are set forth in the Examples.

EXAMPLES

Reference is now made to the following examples for a more detailed explanation of the preferred embodiments of the invention.

Example 1

Glass NZP (Na₂ O-ZnO-P₂ O₅) with 42.1 mol % Na₂ O, 16.5 mol % ZnO and 41.4 mol % P₂ O₅ has been prepared from NH₄ H₂ PO₄ (ammonium dihydrogen phosphate) mixed with ZnO and Na₂ CO₃. After mixing, the batch was placed in a platinum crucible and heated to 300° C. to calcine and release the ammonia and water vapors. The calcined batch was then heated to a temperature of 900° C. and held there for three hours. After melting, the glass was cast into cullet on a cold brass mold. The cullet was then remelted in a glove box furnace and cast into a rotating preform mold at 260° C. to form an overcladding tube for the preform. The molten fluoride cladding composition was rotationally cast ino this oxide glass tube, and subsequently the tube was filled with the molten fluoride core composition. After annealing, the preform investigated was inspected for crystals at the clad-overclad interface; no such crystals were found. The fluoride glass clad was a six component ZrF₄ -HfF₄ -Ba₂ F-LaF₃ -AlF₃ NaF (ZHBLAN) composition, while the core was ZrF₄ -BaF₂ LaF₃ -A1F₃ NaF (ZBLAN) composition.

The NZP oxide glass transition temperature, measured by DSC, was 264° C. This temperature is very close to that of conventional ZBLAN glass. Other ZBLAN fluoride glass compositions, as disclosed in U.S. Pat. No. 4,445,755, can also be used in this invention. The ZBLAN glass disclosed above has a glass transition temperature of 260° C. and a linear coefficient of expansion of 16.7×10⁻⁶ ° C.⁻¹. The linear coefficient of expansion of the oxide overclad glass is similar to that of the ZHBLAN and ZBLAN glasses.

Fiber has been drawn from this preform to verify the compatibility of the thermal properties of the three glasses. The fiber draw was conducted at slightly higher drawing temperatures compared with those used for preforms containing only fluoride glass (400° C. instead of 360° C.).

A 200 micron diameter fiber approximately 500 m long was drawn from the preform. Tests on this fiber show that the median strength is approximately double that of a ZBLAN glass fiber without the oxide glass coating. The coated fiber was also found to be much less fragile during stripping, cleaving and other normal handling operations compared to similar uncoated fluoride fibers.

Also, on immersion in water, the oxide glass showed only slight attack after four hours at 20° C., while a similar fluoride glass was attached after only 30 minutes.

Example 2

Glass KNZP (K₂ O-Na₂ O-ZnO-P₂ O₅) with 21 mol % K₂ O, 21 mol % Na₂ O, 16.5 mol % ZnO and 41.5 mol % P₂ O₅ was prepared. The mixed alkali effect was found to lower the T_(g) of this glass to 230° C., approximately 30° C. lower than that of the NZP glass described in Example 1.

Because of its lower T_(g) and lower viscosity, KNZP glass was found more suitable for overcladding of a fluoride preform, since the fiber draw temperature could be further lowered. This further minimizes the risk of core glass crystallization at elevated temperature.

This oxide glass gave excellent results as a clad on the ZBLAN fluoride glass core.

Example 3

An oxide glass LNZP-1 ((Li₂ O-Na₂ O_(ZnO-P) ₂ O₅) with 21 mol % Li₂ O, 21 mol % Na₂ O, 16.5 mol % ZnO and 41.5 mol % P₂ O₅ was prepared and used as a coating for a fluoride fiber. The Tg of this oxide glass is 256° C., and the linear thermal expansion coefficient is 17.4×10⁻⁶ ° C.⁻¹. The viscosity of this oxide glass is approximately the same as that of the ZBLAN glass at the drawing temperature, i.e., about 10⁶ poise at 302° C.

This oxide glass gave excellent results as a clad on a ZBLAN fluoride glass core or a ZBLAN core and ZHBLAN clad.

Example 4

An oxide glass of composition KNZP described above as used to form a cladding tube having refractive index of 1.492. A core was made of a ZrF₄ -BaF₂ LaF₃ AlF₃ (ZBLA) glass having a refractive index of 1.515. This glass pair gives a fiber having a nominal numerical aperture (NA) of about 0.26.

Preforms of this sort consisting of an oxide glass clad and a fluoride glass core can be used to fabricate optical fiber for short wavelength applications, i.e., at wavelengths of about 2 microns or less.

Again, the clad is compatible with the fluoride core and provides acceptable performance.

While it is apparent that the invention herein disclosed is well calculated to fulfill the objects above stated, it will be appreciated that numerous modifications and embodiments may be devised by those skilled in the art, and it is intended that the appended claims cover all such modifications and embodiments as fall within the true spirit and scope of the present invention. 

What is claimed is:
 1. A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises:preparing a preform comprising a non-oxide glass core, a non-oxide cladding therefore, and a protective coating of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of less than about 19×10⁻⁶ ° C.⁻¹ ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
 2. The method of claim 1 wherein the oxide glass coating is initially formed as a tube and the non-oxide glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
 3. The method of claim 2 wherein the core comprises a heavy metal fluoride glass and is added to the tube as a rod or by casting.
 4. The method of claim 2 wherein the cladding comprises a fluoride glass which is added to the preform after the oxide glass tube is formed.
 5. The method of claim 1 which further comprises initially forming a tube of said oxide glass from an alkali-boro-phosphate or alkali-Group II metal-phosphate composition.
 6. The method of claim 1 which further comprises adding to said oxide glass one or more additional oxide components to impart a specific property to the oxide glass composition.
 7. A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises:preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10⁻⁶ ° C.⁻¹ ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore and at a temperature range of between about 300° and 425° C., said oxide glass having a viscosity which is approximately the same as the viscosity of the fluoride glass at the drawing temperature to obtain said coated optical fiber.
 8. The method of claim 7 wherein the oxide glass coating is initially formed as a tube and the fluoride glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
 9. The method of claim 8 wherein the fluoride glass is added to the tube as a rod, by casting or by chemical vapor deposition.
 10. The method of claim 7, wherein the preform further comprises a fluoride glass cladding between the core and overclad, which cladding is added to the preform after the oxide glass tube is formed, so that the oxide glass overclad is used as a protective coating for said core and cladding.
 11. The method of claim 9 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
 12. A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises:preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass of a phosphate material having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10⁻⁶ ° C.⁻¹ ; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
 13. The method of claim 12 wherein the oxide glass is formed as a tube of an alkali-boro-phosphate or alkali-alkaline earth-phosphate composition having a thermal expansion coefficient between about 15 and 19×10⁻⁶ ° C.⁻¹.
 14. The method of claim 12 which further comprises adding to said oxide glass one or more additional oxide forming components to impart a specific property to the oxide glass composition.
 15. The method of claim 12 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
 16. A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises:preparing a preform which comprises a non-oxide glass core and an overclad of an oxide glass having a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10⁻⁶ ° C.⁻¹ by initially melting the oxide glass coating; rotating said molten oxide glass to form a tube of oxide glass; and placing the non-oxide glass into the tube of oxide glass to form the preform; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
 17. The method of claim 16 wherein the rotating of said molten oxide glass is effected by casting said molten oxide glass into rotating mold means to form said tube.
 18. The method of claim 17 wherein said non-oxide glass is a heavy metal fluoride glass and the fiber is drawn at a temperature range of about 300° and 425° C.
 19. The method of claim 16 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding.
 20. A method for making a coated optical fiber which is resistant to water or water vapor during preform handling, fiber drawing and fiber usage which comprises:preparing a preform which comprises a non-oxide glass core of a heavy metal fluoride glass and an overclad of an oxide glass of a phosphate material; and drawing a fiber from said preform in a draw furnace without a protective atmosphere therefore, said oxide glass having a viscosity which is approximately the same as the viscosity of the non-oxide glass at the drawing temperature to obtain said coated optical fiber.
 21. The method of claim 20 wherein said phosphate oxide glass has a glass transition temperature below about 400° C. and a thermal expansion coefficient of below about 19×10⁻⁶ ° C.⁻¹.
 22. The method of claim 21 wherein the oxide glass is formed as a tube of an alkali-boro-phosphate or alkali-alkaline earth-phosphate composition having a thermal expansion coefficient between about 15 and 19×10⁻⁶ ° C.⁻¹.
 23. The method of claim 22 which further comprises adding to said oxide glass one or more additional oxide forming components to impart a specific property to the oxide glass composition.
 24. The method of claim 23 wherein said non-oxide glass is a heavy metal fluoride glass and the fiber is drawn at a temperature range of about 300° and 425° C.
 25. The method of claim 24 wherein the oxide glass coating is initially formed as a tube and the fluoride glass core in the form of a solid, liquid or gas is placed into the tube prior to the drawing step.
 26. The method of claim 25 wherein the fluoride glass is added to the tube as a rod or by chemical vapor deposition.
 27. The method of claim 25 wherein the preform further comprises a fluoride glass cladding between the core and overclad, which cladding is added to the preform after the oxide glass tube is formed so that the oxide glass overclad is used as a coating for said core and cladding.
 28. The method of claim 25 wherein the rotating of said molten oxide glass is effected by casting said molten oxide glass into rotating mold means to form said tube.
 29. The method of claim 20 wherein the oxide glass has a refractive index sufficiently less than that of said core so as to act as a cladding. 